- Features
- Excellent dimensional stability.
- No deformation in sizes.
- No decrease in hardness and physical characteristics.
2. Types of MC
| Types | MC-C | MC-D | MC-H4 | MC-H | T-MC | |
|---|---|---|---|---|---|---|
| Hardness range | 25~50 | 20~55 | 40~60 | 15~50 | 35~50 | |
| Color | Blue | Blue-green | Blue | |||
| Main Features | *For general use | *Abrasion resistance *Bleedless | *Edging resistance *Abrasion resistance | *Edging resistance *Abrasion resistance *Good coating performance *Low hardness | *For general use *Bleedless | |
| Tin plate varnishing | For spot | Excellent (For white coating) | Good | Excellent (For varnishing) | Excellent | |
| For solid | Excellent | Excellent | Excellent | |||
| For stripe | Good | Excellent | ||||
| Varnishing on papers | Good | Excellent | ||||
| Tin plate coating | Good | Excellent | ||||
| Plywood coating | Good | Excellent | ||||
3. Solvent resistance
| MC-C 35 | MC-D 35 | MC-H 30 | ||
|---|---|---|---|---|
| Volatile Solvent | 2Hours | 0 | 0 | 0 |
| 5Hours | 0 | 0 | 0 | |
| 24Hours | 0 | 0 | 0 | |
| 48Hours | -2 | 0 | -2 | |
| 50°Cdry | -4 | -4 | -4 | |
| Methyl ethyl ketone | 2Hours | 18 | 18 | 18 |
| 5Hours | 254 | 26 | 26 | |
| 24Hours | 32 | 44 | 40 | |
| 48Hours | 30 | 46 | 40 | |
| 50°Cdry | -16 | -8 | -14 | |
| Acetic ether | 2Hours | 14 | 16 | 16 |
| 5Hours | 22 | 24 | 26 | |
| 24Hours | 34 | 40 | 42 | |
| 48Hours | 34 | 48 | 46 | |
| 50°Cdry | -14 | -4 | -8 | |
| Toluene | 2Hours | 2 | 2 | 2 |
| 5Hours | 2 | 2 | 2 | |
| 24Hours | 4 | 6 | 4 | |
| 48Hours | 4 | 6 | 4 | |
| 50°Cdry | -4 | -2 | -2 |
【Test Method】Solvent test:1g block compound. Temperature... 20°C
4. Other applications
- Cleaning rolls used with solvent. (MC-C, MC-D)
- Printing rolls with solvent type inks. (MC-C)
- Resist coating roller for PCB(Print Circuit Board)
NOTE: Do not use for the following applications;
- Use of chemical that includes a lot of acid, alkali, etc., urethane type adhesives and paint.
- Use of paint which includes only ketone, or ethyl acetate or trichlene.
- When nip pressure given to rubber roller is extremely high.